Experimental and numerical study of damage caused by high-current electron beam of construction materials intended for the first wall of powerful plasma installations

封面

如何引用文章

全文:

开放存取 开放存取
受限制的访问 ##reader.subscriptionAccessGranted##
受限制的访问 订阅或者付费存取

详细

An experimental study of the effect of high-current electron beams on crystals made of polycrystalline tungsten and corrosion-resistant ferritic-martensitic steel EK-181 was carried out, as well as a numerical simulation of the process of interaction of the beam with the target, in which the energy of the electron beam is absorbed in the near-surface layers of the samples under study. The experiments are carried out on the Kalmar high-current electron accelerator at an average pulse energy of E ≈ 100 ± 20 J (pulse duration at half maximum 100 ns). During the experiments, samples were irradiated from one to ten times. In the numerical modeling, electron spectra were used, calculated on the basis of data (currents and voltages in the diode gap) obtained as a result of electrical measurements. The difference in the nature of destruction of tungsten and steel was demonstrated. It has been shown that tungsten begins to crack after three-pulse exposure with an energy of about 100 J, which correlates well with tests on other types of installations. On steel, minor cracking was observed only after 8–10 pulses of exposure. Numerous traces of droplets of melting and redeposition of the target material were found on the surface of the steel target. For both materials, the specific amount of energy that is absorbed in the region of interaction of the electron beam with the target is estimated.

全文:

受限制的访问

作者简介

N. Bobyr

NRC “Kurchatov Institute”

Email: Kazakov_ED@nrcki.ru
俄罗斯联邦, Moscow, 123182

E. Kazakov

NRC “Kurchatov Institute”; Keldysh Institute of Applied Mathematics RAS; Moscow Institute of Physics and Technology (National Research Institute)

编辑信件的主要联系方式.
Email: Kazakov_ED@nrcki.ru
俄罗斯联邦, Moscow, 123182; Moscow, 125047; Dolgoprudny, 141701

M. Orlov

NRC “Kurchatov Institute”

Email: Kazakov_ED@nrcki.ru
俄罗斯联邦, Moscow, 123182

A. Smirnova

NRC “Kurchatov Institute”; Keldysh Institute of Applied Mathematics RAS; Moscow Institute of Physics and Technology (National Research Institute)

Email: anya4113@gmail.com
俄罗斯联邦, Moscow, 123182; Moscow, 125047; Dolgoprudny, 141701

A. Spitsyn

NRC “Kurchatov Institute”

Email: Kazakov_ED@nrcki.ru
俄罗斯联邦, Moscow, 123182

M. Strizhakov

NRC “Kurchatov Institute”

Email: Kazakov_ED@nrcki.ru
俄罗斯联邦, Moscow, 123182

K. Sunchugashev

Peoples’ Friendship University of Russia

Email: Kazakov_ED@nrcki.ru
俄罗斯联邦, Moscow, 117198

S. Tkachenko

NRC “Kurchatov Institute”; Keldysh Institute of Applied Mathematics RAS; Moscow Institute of Physics and Technology (National Research Institute); Joint Institute for High Temperatures, Russian Academy of Sciences

Email: Kazakov_ED@nrcki.ru
俄罗斯联邦, Moscow, 123182; Moscow, 125047; Dolgoprudny, 141701; Moscow, 125412

参考

  1. Будаев В.П. // Вопросы атомной науки и техники. Сер. термоядерный синтез. 2015. Т. 38. Вып. 4. С. 5. https://www.doi.org/10.21517/0202-3822-2015-38-4-5-332
  2. Martynenko Y.V., Budaev V.P., Grashin S.A., Shestakov E.A. // Bulletin of the Lebedev Physics Institute. 2017. V. 44(6). P. 182. https://www.doi.org/10.3103/S1068335617060070
  3. Zhitlukhin A., Klimov N., Landman I., Linke J., Loarte A., Merola M., Podkovyrov V., Federici G., Bazylev B., Pestchanyi S., Safronov V., Hirai T., Maynashev V., Levashov V., Muzichenko A. // J. Nucl. Mater. 2007. V. 363–365. P. 301. https://www.doi.org/10.1016/j.jnucmat.2007.01.027
  4. Martín-Solís J.R., Loarte A., Lehnen M. // Nuclear Fusion. 2017. V. 57. № 6. P. 066025. https://www.doi.org/10.1088/1741-4326/aa6939
  5. Бобырь Н.П., Казаков Е.Д., Крутиков Д.И., Курило А.А., Орлов М.Ю., Спицын А.В., Стрижаков М.Г. // Ядерная физика и инжиниринг. 2022. Т. 13. № 2. С. 113. https://www.doi.org/10.56304/S2079562922010092
  6. Поскакалов А.Г., Климов Н.С., Гаспарян Ю.М., Огородникова О.В., Ефимов В.С. // Вопросы атомной науки и техники. Сер. термоядерный синтез. 2018. Т. 41. № 1. С. 23. https://www.doi.org/10.21517/0202-3822-2017-41-1-23-28
  7. Гаркуша И.Е., Малыхин С.В., Махлай В.А., Пугачев А.Т., Баздырева С.В., Аксенов Н.Н. // Журнал технической физики. 2014. Т. 84. № 11. С. 41.
  8. Позняк И.М., Сафронов В.М., Цыбенко В.Ю. // Вопросы атомной науки и техники. Сер. термоядерный синтез. 2016. Т. 39. № 1. С. 15. https://www.doi.org/10.21517/0202-3822-2016-1-15-21
  9. Голубева А.В., Коваленко Д.В., Лиджигоряев С.Д., Барсук В.А., Бобырь Н.П., Медников А.А., Климов Н.С., Хуанг К., Терентьев Д., Ашикава Н., Чернов В.М. // Поверхность. Рентген. синхротр. и нейтрон. исслед. 2022. № 1. С. 30. https://www.doi.org/10.31857/S102809602201006X
  10. Демидов Б.А., Мартынов А.И. // Журнал экспериментальной и теоретической физики. 1981. Т. 80. № 2. С. 738.
  11. Аккерман А.Ф., Бушман А.В., Демидов Б.А., Ивкин М.В., Ни А.Л., Петров В.А., Рудаков Л.И., Фортов В.Е. // Журнал экспериментальной и теоретической физики. 1986. Т. 91. № 3. С. 1762.
  12. Демидов Б.А. // Физика плазмы. 2003. Т. 29. № 7. С. 670.
  13. Демидов Б.А., Ефремов В.П., Петров В.А., Мещеряков А.Н. // Поверхность. Рентген. синхротр. и нейтрон. исследования. 2009. № 9. С. 18.
  14. Садовничий Д.Н., Милехин Ю.М., Калинин Ю.Г., Казаков Е.Д., Лавров Г.С., Шереметьев К.Ю. // Физика горения и взрыва. 2022. Т. 58. № 2. С. 88. https://www.doi.org/10.15372/FGV20220210
  15. Демидов Б.А., Ивкин М.В., Петров В.А., Фанченко С.Д. // Атомная энергия. 1979. Т. 46. Вып. 2. с. 101.
  16. Милехин Ю.М., Садовничий Д.Н., Шереметьев К.Ю., Калинин Ю.Г., Казаков Е.Д., Марков М.Б. // Доклады академии наук. 2019. Т. 487. № 2. C. 159.
  17. Демидов Б.А., Казаков Е.Д., Калинин Ю.Г., Крутиков Д.И., Курило А.А., Орлов М.Ю., Стрижаков М.Г., Ткаченко С.И., Чукбар К.В., Шашков А.Ю. // Приборы и техника эксперимента. 2020. № 3. С. 90. https://www.doi.org/10.31857/S003281622003009X
  18. Бойко В.И., Валяев А.Н., Погребняк А.Д. // Успехи физических наук. 1999. Т. 169. № 11. С. 1243. https://doi.org/10.1070/PU1999v042n11ABEH000471
  19. Молодец А.М., Савиных А.С., Голышев А.А., Гаркушин Г.В., Шилов Г.В., Некрасов А.Н. // Физика металлов и металловедение. 2022. Т. 123. № 5. С. 554.
  20. Павленко А.В., Малюгина С.Н., Майорова А.С., Мокрушин С.С., Казаков Д.Н., Филатов С.Ю. Температурно-скоростные зависимости прочностных характеристик стали ЭК-181. // Труды “Забабахинских научных чтений”. 2019. С. 141.
  21. Кириллов А. К., Лаппа А. В., Пляшешников А. В., Щербакова Л. В. Программа расчета методом Монте-Карло электронно-фотонных полей в гетерогенных осесимметричных средах. 80/6 “Каскад”. Челябинск: ЧГУ, 1982.
  22. Berger M.J. Methods in Computational Physics. V. 1. New York: Academic Press, 1963. P. 135.
  23. Аккерман А.Ф., Никитушев Ю.М., Ботвин В.А. Решение методом Монте-Карло задач переноса быстрых электронов в веществе. Алма-Ата: Наука, 1972. С. 166.
  24. Пляшешников А. В., Кольчужкин А. М. // Атомная энергия. 1976. Т. 41. Вып. 6. С. 415.
  25. Григорьев И.С., Мейлихов Е.З. Физические величины. Справочник. М.: Энергоатомиздат, 1991.

补充文件

附件文件
动作
1. JATS XML
下载
2. Fig. 1. Typical time dependence of the power of an electron beam with an energy of 120 (1); 100 (2) and 80 J (3), irradiating a sample.

下载 (15KB)
索引源数据
3. Fig. 2. Images of the surface of tungsten targets after 3 (a) and 10 (b) exposures to an electron beam.

下载 (41KB)
索引源数据
4. Fig. 3. Images of the surface of steel targets after 6 (a) and 10 (b) exposures to an electron beam.

下载 (35KB)
索引源数据
5. Fig. 4. The fraction of electrons Ne whose energy dropped below the tracking threshold after interaction with the target, and the fraction of the beam energy absorbed by the target E depending on the distance to the irradiated surface of the target X in samples made of steel (a) and tungsten (b) with a thickness of 1 mm.

下载 (62KB)
索引源数据
6. Fig. 5. The fraction of electrons Ne whose energy dropped below the tracking threshold after interaction with the target, and the fraction of the beam energy absorbed by the target E depending on the distance to the irradiated target surface X in the 100 μm thick near-surface layer of steel (a) and tungsten (b) samples.

下载 (30KB)
索引源数据

版权所有 © Russian Academy of Sciences, 2024